Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.23 g/cm³ |
| Water absorption rate | | ISO62 | 0.70 % |
| Water absorption rate | | ISO62 | 0.20 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 无断裂 |
| Charpy Notched Impact Strength | | ISO179/1eA | 9.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 45 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 2200 MPa |
| Tensile stress | | ISO527-2/50 | 55.0 MPa |
| Tensile strain | | ISO527-2/50 | 6.0 % |
| Nominal tensile fracture strain | | ISO527-2/50 | 75 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+15 ohms |
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 17 kV/mm |
| | IEC60250 | 3.10 |
| Dissipation Factor | | IEC60250 | 0.020 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO75-2/B | 120 °C |
| Heat distortion temperature | | ISO75-2/A | 105 °C |
| maximum service temperature | | IEC216 | 110 °C |
| maximum service temperature | | | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.