PA6 40 Grupa Azoty ATT Polymers GmbH
0
- Usages:Thin filmmonofilament
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 1.4 % | |
| Water absorption rate | ISO 62 | 2.0/10 % | |
| density | ISO 1183 | 1.14 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 1.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ISO 180/1U | NB kJ/m² | |
| tensile strength | ISO 527-2 | 85 MPa | |
| elongation at break | ISO 527-2 | >100 % | |
| Tensile modulus | ISO 527-2 | 2900 MPa | |
| Impact strength of cantilever beam gap | ISO 180/1A | 6.50 kJ/m² |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-2 0.80mm | |
| UL -94 | V-2 1.50mm | ||
| UL -94 | V-2 3.00mm | ||
| GWIT | IEC 60695-2-12 | 825 °C |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+14 Ω.cm | |
| Dissipation Factor | IEC 60112 | >600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/Bf | 180 °C | |
| ISO 75-2/Af | 80 °C | ||
| vicat | ISO 306/B50 | 208 °C | |
| Melting Temperature | ISO 11357-3 | 222 °C | |
| Linear coefficient of thermal expansion | 80 °C | ||
| IEC 60695-10-2 | >165 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.