POM NW-02 JAPAN POLYPLASTIC

Form：Granules | Grade：Injection grade

Properties:

High slidingwear resistant

Typical Applications:

Electrical fieldElectronic fieldFitness equipmentAutomotive sectorBottle cap

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Electrical field \| Electronic field \| Fitness equipment \| Automotive sector \| Bottle cap
Properties:	High sliding \| wear resistant

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.9	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Wear factor	0.060MPa,0.15m/sec7	JISK7218	1000	10^-8mm³/N·m
	Wear factor	0.060MPa,0.15m/sec6	JISK7218	300	10^-8mm³/N·m
		Wear factor	0.98MPa,0.30m/sec5	JISK7218	19	10^-8mm³/N·m
		Wear factor	Wear factor	0.98MPa,0.30m/sec4	JISK7218	<1.0	10^-8mm³/N·m
Friction coefficient	Steel - Dynamic3	JISK7218	0.17
Friction coefficient	Friction coefficient	Dynamic2	JISK7218	0.37
bending strength		ISO 178	72.0	Mpa
Bending modulus		ISO 178	2200	Mpa
Nominal tensile fracture strain		ISO 527-2	20	%
tensile strength		ISO 527-2	52.0	Mpa
Tensile modulus		ISO 527-2	2350	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	85.0	°C
Linear coefficient of thermal expansion	TD：23to55°C	Internal Method	1.2E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C	Internal Method	1.2E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23°C,24hr	ISO 62	0.70	%
Shrinkage rate	MD:2.00mm	ISO 294-4	2.0	%
Shrinkage rate	Shrinkage rate	TD:2.00mm	ISO 294-4	1.8	%
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	18.0	cm3/10min
melt mass-flow rate	190°C/2.16kg	ISO 1133	20	g/10min
density		ISO 1183	1.36	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength	3.00mm	IEC 60243-1	20	KV/mm
Volume resistivity		IEC 60093	1E+14	ohms·cm
Surface resistivity		IEC 60093	3E+15	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ISO 2039-2	70
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ColourNumber			CF2001/CD3501

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.