Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.80 g/cm³ |
| Shrinkage rate | | | 0.20到0.50 % |
| Water absorption rate | Equilibrium | | 0.020 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | | 110 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compressive strength | | | 110 MPa |
| tensile strength | | | 150 MPa |
| elongation | Break | | 2.5 % |
| Flexural modulus | | | 17000 MPa |
| bending strength | | | 220 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | | 10.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | | 8E+15 ohms |
| Volume resistivity | | | 5E+16 ohms·cm |
| dielectric strength | | | 15 kV/mm |
| dielectric constant | | | 5.00 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | | 267 °C |
| melting temperature | | | 288 °C |
| | | 1.8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.