Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 0.80 0.80 |
| Shrinkage rate | | % | 0.40 0.40 |
| Water absorption rate | | % | 1.2 1.2 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 114 101 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | V-0 V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 7300 5100 |
| Tensile stress | | MPa | 121 87.0 |
| Tensile strain | | % | 2.3 2.5 |
| Flexural modulus | | MPa | 6700 |
| Bending stress | | MPa | 169 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | kJ/m² | 37 56 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+15 -- |
| dielectric strength | | kV/mm | 28 -- |
| dielectric constant | | | 3.60 -- |
| Dissipation Factor | | | 0.020 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | | °C | 246 -- |
| Heat Deflection Temperature | | °C | 223 -- |
| Linear thermal expansion coefficient | | cm/cm/°C | 4E-05 4E-05 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare