PA6 LUBEMID B27 NATURAL HS

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183/A	1.11to1.15 g/cm³
Water absorption rate		ISO 62	2.0 %

flammability	Test Condition	Test Method	Test Result
Burning wire flammability index		IEC 60695-2-12	750 °C

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D256	无断裂
	Impact strength of cantilever beam gap		ASTM D256	4.5to6.0 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180/A	4.5to6.5 kJ/m²
Suspended wall beam without notch impact strength		ISO 180	无断裂
Charpy Notched Impact Strength		ISO 179/1eA	4.5to6.5 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	无断裂
Impact strength of cantilever beam gap		ASTM D256A	45to60 J/m

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1A/1	3200to3800 MPa
tensile strength	Yield	ISO 527-2/1A/50	55.0to75.0 MPa
tensile strength	tensile strength	Break	ISO 527-2/1A/50	40.0to60.0 MPa
Tensile strain	Yield	ISO 527-2/1A/50	7.0to12 %
Tensile strain	Tensile strain	Break	ISO 527-2/1A/50	20to25 %
Flexural modulus		ISO 178	2000to2500 MPa
bending strength		ISO 178	60.0to80.0 MPa

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ASTM D648	155to165 °C
	Heat distortion temperature		ISO 75-2/B	160to170 °C
	Heat distortion temperature	Heat distortion temperature		ASTM D648	55.0to65.0 °C
vicat		ISO 306/A120	205to215 °C
vicat	vicat		ISO 306/B120	200to210 °C
melting temperature		内部方法	210to225 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.