Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.20 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 25.0 cm3/10min |
| Shrinkage rate | | 内部方法 | 0.50-0.70 % |
| Shrinkage rate | | 内部方法 | 0.50-0.70 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTM D542 | 1.585 |
| transmissivity | | ASTM D1003 | 88.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | V-2 |
| Burning wire flammability index | | IEC 60695-2-12 | 825 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 875 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 850 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 875 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 2400 Mpa |
| tensile strength | | ISO 527-2/50 | 62.0 Mpa |
| Tensile strain | | ISO 527-2/50 | 6.0 % |
| Nominal tensile fracture strain | | ISO 527-2/50 | >50 % |
| Flexural modulus | | ISO 178 | 2400 Mpa |
| bending strength | | ISO 178 | 95.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 53 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 30 KV/mm |
| relative permittivity | | IEC 60250 | 3.10 |
| relative permittivity | | IEC 60250 | 3.00 |
| Dissipation Factor | | IEC 60250 | 1E-03 |
| Dissipation Factor | | IEC 60250 | 9E-03 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI Elec | | UL 746 | 125 °C |
| RTI Imp | | UL 746 | 115 °C |
| RTI Str | | UL 746 | 125 °C |
| Heat distortion temperature | | ISO 75-2/B | 136 °C |
| Heat distortion temperature | | ISO 75-2/A | 123 °C |
| vicat | | ISO 306/B50 | 142 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 7E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.