Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTMD955 | 0.20到0.50 % |
| density | | ASTMD792 | 1.15 g/cm³ |
| Apparent density | | ASTMD1895 | 0.66 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 3.0 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTMD785 | 60 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | ASTMD1003 | 2.7 % |
| Yellowness Index | | ASTMD1925 | 2.5 YI |
| gloss | | ASTMD2457 | 120 |
| transmissivity | | ASTMD1003 | 92.5 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTMD638 | 65.5 MPa |
| elongation | Yield | ASTMD638 | 3.0 % |
| Flexural modulus | | ASTMD790 | 3380 MPa |
| bending strength | Yield | ASTMD790 | 96.5 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 270 J/m |
| film | Test Condition | Test Method | Test Result |
|---|
| oxygen permeability | | ASTMD3985 | 0.31 cm³·mm/m²/atm/24hr |
| Water vapor permeability | | ASTMF1249 | 2.0 g·mm/m²/atm/24hr |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 68.9 °C |
| | ASTMD648 | 76.7 °C |
| | ASTMD696 | 6.7E-05 cm/cm/°C |
| specific heat | | ASTMC351 | 1340 J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.25 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.