PP Homopolymer BFI 4170
0
- Usages:film
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D1505 | 0.905 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 0.75 g/10min |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | Blown Film | ASTM D1709A | 350 g |
| Elmendorf tear strength | ASTM D1922 | 55 g | |
| ASTM D1922 | 300 g | ||
| OTr | ASTM D3985 | 53 cm³·mm/m²/atm/24hr | |
| Water Vapor Transmission Rate | ASTMF1249 | 0.18 g·mm/m²/atm/24hr | |
| Secant modulus | ASTM D882 | 689 MPa | |
| ASTM D882 | 600 MPa | ||
| tensile strength | ASTM D882 | 26.2 MPa | |
| ASTM D882 | 24.8 MPa | ||
| ASTM D882 | 58.6 MPa | ||
| ASTM D882 | 37.9 MPa | ||
| elongation | ASTM D882 | 750 % | |
| ASTM D882 | 770 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | DSC | 160to165 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.