PPS HGR20
33
- Properties:Dimensional stabilityLow friction coefficienthigh strengthArc resistanceAnti gamma radiationEasy to processCreep resistanceAntichemicalLow shrinkageFlame retardant
- Usages:Electrical componentsElectrical appliancesMilitary applicationsLaptop caseElectronic fieldElectrical field
Compare
View PricesTechnical Data Sheet
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| combustibility | 级 | GB/T 2408-1996 FV-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | % | GB/T 15585-1995 | |
| compressive strength | MPa | GB/T 1041-1992 | |
| Rockwell hardness | hr | GB/T 9342-1988 | |
| tensile strength | MPa | GB/T 1040-1992 | |
| elongation | % | GB/T 1040-1992 | |
| Flexural modulus | MPa | GB/T 9341-2000 | |
| bending strength | MPa | GB/T 9341-2000 172 | |
| Impact strength of cantilever beam gap | KJ/m | GB/T 1843-1996 | |
| elongation at break | ASTM D638/ISO 527 | 1.8 % | |
| tensile strength | ASTM D638/ISO 527 | 120 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 100 | |
| Flexural modulus | ASTM D790/ISO 178 | 1.15*100000 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 172 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | MHz | GB/T 1409-1988 | |
| electric strength | kV/mm | GB/T 1408.1-1999 | |
| Volume resistivity | Ω.M | GB/T 1410-1989 | |
| Surface Resistivity | Ω | GB/T 1410-1989 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.51 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ℃ | GB/T 1634.2-2004 | |
| melting point | 281 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.