Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.27 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 26.0 cm³/10min |
| Shrinkage rate | | ISO 294-4 | 0.60 % |
| Water absorption rate | | ISO 62 | 0.35 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | IEC 60695-11-10,-20 | V-0 |
| Flammability level | | IEC 60695-11-10,-20 | V-1 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 2500 MPa |
| tensile strength | Yield | ISO 527-2 | 60.0 MPa |
| Tensile strain | Yield | ISO 527-2 | 5.0 % |
| Nominal tensile fracture strain | | ISO 527-2 | >50 % |
| Flexural modulus | | ISO 178 | 2400 MPa |
| bending strength | | ISO 178 | 90.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 20 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 50 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | | ISO 180/4A | 20 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/4A | 55 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| relative permittivity | | IEC 60250 | 3.00 |
| Dissipation Factor | | IEC 60250 | 5E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 104 °C |
| vicat | | ISO 306/B50 | 110 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.