AS(SAN)

AS(SAN) 52485 Thailand ZNEOS

Compare

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result
melt mass-flow rate	220℃,10kg	ISO 1133	23 g/10min
density	Natural	ISO 1183	1.08 Natural

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Speed 2mm/min	ISO 178	111 Mpa
Rockwell hardness	t=6.4mm	ISO 2039-2	126 R scale
tensile strength	Yield,Speed 50mm/min	ISO 527	68 Mpa
Tensile modulus	Speed 1mm/min	ISO 527	3.7 GPa
Bending modulus	Speed 2mm/min	ISO 178	2.8 GPa
tensile strength	Speed 50mm/min，Break	ISO 527	3.2 %
Impact strength of cantilever beam gap	23℃	ISO 180	2.0 KJ/m

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	5kg,120℃/hr	ISO 306	104 °C
Hot deformation temperature	Method A	ISO 75	84 °C
UL flame retardant rating		UL 94	HB
Hot deformation temperature	Method B	ISO 75	96 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate		ASTM D-955	0.3-0.4 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.