PP TRANSMARE® 10HGB30-0.001

Properties:
Filler
glass beads
30%
filler by weight
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO1183	1.10 g/cm³
melt mass-flow rate		ISO1133	7.0 g/10min

hardness	Test Condition	Test Method	Test Result
		ISO868	78

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO179/1U	13 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO179/1U	27 kJ/m²
Impact strength of cantilever beam gap		ISO180/1A	2.1 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO180/1A	2.5 kJ/m²
		ISO180/1U	12 kJ/m²
			ISO180/1U	22 kJ/m²
Charpy Notched Impact Strength		ISO179/1A	1.2 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO179/1A	2.1 kJ/m²

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO527-2/1	2300 MPa
Tensile stress		ISO527-2/50	30.0 MPa
Tensile stress	Tensile stress		ISO527-2/50	28.0 MPa
TensileStrain		ISO527-2/50	3.7 %
Tensile strain		ISO527-2/50	7.2 %
Flexural modulus		ISO178	2100 MPa
Bending stress		ISO178	45.0 MPa

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO75-2/B	91.0 °C
Heat distortion temperature	Heat distortion temperature		ISO75-2/A	51.0 °C
vicat		ISO306/A	155 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.