ABS HP-181 BK CNOOC&LG HUIZHOU

268

Form：Granules

Properties:

High impactHigh mobilityHigh glossUniversal level

Typical Applications:

Wear resistant accessoriesElectronic appliancescontainerchip

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Wear resistant accessories \| Electronic appliances \| container \| chip
Properties:	High impact \| High mobility \| High gloss \| Universal level

Certificates

No Data...

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTMD785	106
Izod Notched Impact Strength	6.4mm(Notched) 23℃	ASTMD256	26	kg.cm/cm
Bending modulus	6.4mm 10mm/min	ASTMD790	24000	kg/cm2
bending strength	6.4mm 10mm/min	ASTMD790	630	kg/cm2
Elongation at Break	3.2mm @Break 50mm/min	ASTM D638	18	%
tensile strength	3.2mm @Yield 50mm/min	ASTM D638	450	kg/cm2
Injection Molding Guide	Test Condition	Test Method	Test Result	Test Unit
Screw speed			30~60	rpm
Back pressure			10~30	kg/cm2
Mold temperature			40~80	℃
Melting temperature			200-240	℃
Pre drying time			3~4	hrs
Pre drying temperature			70~80	℃
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	6.4mm(Unanneald) 1.82MPa	ASTMD648	82	℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220℃/10kg	ASTMD1238	40	g/10min
Shrinkage rate	3.2mm	ASTMD955	0.4~0.7	%
density		ASTMD792	1.04	g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.