Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO1133 | 15 g/10min |
| Shrinkage rate | | ISO294-4 | 1.3 % |
| Shrinkage rate | | ISO294-4 | 1.3 % |
| Water absorption rate | | ISO62 | 0.020 % |
| Ash Content | | ISO3451 | 20 % |
| density | | ISO1183 | 1.05 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 75 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/1A | 1.9 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 2.3 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 33 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 2200 MPa |
| Bending stress | | ISO178 | 41.0 MPa |
| Tensile stress | | ISO527-2/20 | 28.0 MPa |
| Tensile stress | | ISO527-2/20 | 23.0 MPa |
| Tensile strain | | ISO527-2/20 | 5.5 % |
| Tensile strain | | ISO527-2/20 | 25 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 110 °C |
| | ISO75-2/A | 57.0 °C |
| vicat | | ISO306/A50 | 149 °C |
| vicat | | ISO306/B50 | 92.0 °C |
| BallPressure Test | | IEC335 | 通过 |
| | ISO11359-2 | 8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.