PA66 20G6201 Changchun Chemical (Zhangzhou)
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ash content | 30 % | ||
| 30 % | |||
| Shrinkage rate | D955 | 0.3-0.8 % | |
| density | D792 | 1.35 g/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 1700 kg/c㎡ | |
| D638 | 167 MPa | ||
| bending strength | D790 | 235 MPa | |
| Flexural modulus | D790 | 7840 MPa | |
| Impact strength of cantilever beam gap | D256 | 14 kg·cm/cm |
| Test Condition | Test Method | Test Result | |
|---|---|---|---|
| density | ASTM D792 | 1.35 - | |
| melting temperature | ASTM DSC | 264 ℃ | |
| Shrinkage rate | ASTM D955 | 0.3-0.8 % | |
| bending strength | ASTM D790 | 2400 kg/c㎡ | |
| Flexural modulus | ASTM D790 | 80000 kg/c㎡ | |
| Impact strength of cantilever beam gap | ASTM D256 | 14 ㎏.㎝/㎝ | |
| Compared to the Leakage Tracking Index (CTI) | ASTM D3638 | PLC 0 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric strength | D149 | 25 kv/mm | |
| Compared to the Leakage Tracking Index (CTI) | D3638 | PLC 0 | |
| dielectric strength | ASTM D149 | 25 kV/㎜ |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | D648 | 256 ℃ | |
| melting temperature | DSC | 264 ℃ | |
| Heat distortion temperature | D648 | 249 ℃ | |
| ASTM D648 | 249 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.