Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 50 g/10min |
| PVLimit2 | | | 300000到400000 psi·fpm |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 99 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2 | 180 Mpa |
| Tensile stress | | ASTMD638 | 194 Mpa |
| elongation | | ASTMD638 | 1.8 % |
| elongation | | ISO527-2 | 1.7 % |
| Flexural modulus | | ASTMD790 | 13500 Mpa |
| Flexural modulus | | ISO178 | 13200 Mpa |
| bending strength | | ASTMD790 | 280 Mpa |
| bending strength | | ISO178 | 260 Mpa |
| compressive strength | | ASTMD695 | 138 Mpa |
| shear strength | | ASTMD732 | 83.0 Mpa |
| Tensile modulus | | ASTMD638 | 13500 Mpa |
| Tensile modulus | | ISO527-2 | 16000 Mpa |
| Friction coefficient 3 | | ASTMD3702 | 0.28 |
| Wear factor | | ASTMD3702 | 46 10^-8mm³/N·m |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ASTMD4812 | 530 J/m |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | | ASTMD3835 | 150 Pa·s |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | ISO11357-2 | 147 °C |
| melting temperature | | ISO11357-3 | 343 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.