Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.08 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 4.0 g/10min |
| Shrinkage rate | | ASTMD955 | 0.20到0.60 % |
| Shrinkage rate | | ASTMD955 | 0.40到0.80 % |
| Water absorption rate | | ISO62 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 113 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Hot filament ignition temperature | | IEC60695-2-13 | 650 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ASTMD638 | 85.0 MPa |
| elongation | Break | ASTMD638 | 3.5 % |
| Flexural modulus | | ASTMD790 | 5200 MPa |
| bending strength | Break | ASTMD790 | 125 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 80 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 120 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC60243-1 | 60 kV/mm |
| | IEC60250 | 2.70 |
| Dissipation Factor | | IEC60250 | 0.0 |
| Surface Resistivity | | IEC60093 | 1E+14 ohms |
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 152 °C |
| vicat | | ASTMD15254 | 140 °C |
| | ISO11359-2 | 3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.