ABS TR-558AI
229
- Properties:transparenthigh strengthHigh impact resistanceHigh strength
- Usages:Electronic fieldElectrical field
- Certificates:UL
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.4-0.7 % | |
| density | ASTM D-792 | 1.11 | |
| melt mass-flow rate | ASTM D-1238（G） | 2.2 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Stretching rate (breaking point) | ASTM D-638 | 40 % | |
| Tension measurement | ASTM D-638 | 22200（2180） kg/cm | |
| Rockwell hardness | ASTM D-785 | 112 | |
| bending strength | ASTM D-790 | 800（78） kg/cm | |
| Impact strength of cantilever beam gap | ASTM D-256 | 10(100) kg.cm/cm(J/m) | |
| Stretching rate (resistance point) | ASTM D-638 | ≥6 % | |
| Tensile strength | ASTM D-638 | 520（51） kg/cm | |
| Bending modulus | ASTM D-790 | 25000(2450) kg/cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| combustibility | IEC 707 | - mm/min | |
| Heat distortion temperature | ASTM D-648 | 95(90) °C | |
| ASTM D-648 | 89(89) °C | ||
| vicat | ASTM D-1525 | 100(93) °C | |
| combustibility | UL -94 | HB CLASS |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.