Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO 62 | 0.09 % |
| Shrinkage rate | | ASTM D-955 | 0.3-0.5 % |
| density | | ISO 1183 | 1.61 g/cm3 |
| processability | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.5-0.9 % |
| spiral flow length | | | -- cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527 | 115 MPa |
| elongation | Break | ISO 527 | 3.8 % |
| bending strength | | ISO 178 | 185 MPa |
| Flexural modulus | | ISO 178 | 7*103 MPa |
| Rockwell hardness | | ASTM D-785 | 90 M scale |
| elongation | | ASTM D-638 | 3.4 % |
| Impact strength of cantilever beam gap | | ASTM D-256 | 50 J/m |
| tensile strength | | ASTM D-638 | 80 MPa |
| Flexural modulus | | ASTM D-790 | 5000 MPa |
| Charpy Notched Impact Strength | | ASTM D-256 | 25 KJ/M2 |
| Charpy Notched Impact Strength | Notched | ASTM D-256 | 7 KJ/M2 |
| bending strength | | ASTM D-790 | 105 MPa |
| Charpy Notched Impact Strength | Notched | ISO 179（leA） | 9 KJ/m2 |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0（0.8mm） |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | IEC 60250 | 3.4 |
| Dielectric loss | | IEC 60250 | 1.8*10-2 |
| Volume resistivity | | ASTM D-257 | 1014 Ω.cm |
| dielectric constant | | ASTM D-150 | 3.0 106Hz |
| Dissipation Factor | | ASTM D-150 | 2.0×10-2 106Hz |
| dielectric strength | | ASTM D-149 | 23 MV/m |
| Volume resistivity | | IEC 60093 | 1*1014 Ω。m |
| dielectric strength | | IEC 60243 | 31 KV/m |
| arc resistance | | IEC 61621 | -- Sec |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| ash content | | | 30 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ASTM D-648 | 170 ℃ |
| | ASTM D-696 | 2.2 10-5℃mm/mm/℃ |
| UL flame retardant rating | | UL 94 | HB V-0 |
| Hot deformation temperature (HDT) | | ISO 75f | 195 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.