PC/ABS NH-1000TG GY Samsung Cheil South Korea

Form：Granules | Grade：Injection grade

Properties:

Flame retardant

Typical Applications:

OA deviceMechanical accessoriesCasters

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	OA device \| Mechanical accessories \| Casters
Properties:	Flame retardant

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	39	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	35	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75mm	UL 94	V-2
	UL flame retardant rating	1.5mm	UL 94	V-1
		UL flame retardant rating	2.0mm	UL 94	V-0
			UL flame retardant rating	3.0mm	UL 94	V-0
			UL flame retardant rating	UL flame retardant rating	2.5mm	UL 94	5VB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/50	2500	Mpa
tensile strength	Yield	ASTM D638	54.0	Mpa
	tensile strength	Yield	ISO 527-2/50	54.0	Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	44.0	Mpa
Tensile strain	Break	ISO 527-2/50	78	%
Bending modulus		ASTM D790	2400	Mpa
Bending modulus	Bending modulus		ISO 178	2700	Mpa
bending strength		ASTM D790	77.0	Mpa
bending strength	bending strength		ISO 178	81.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	86.0	°C
	Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	92.0	°C
		Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	76.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	84.0	°C
Vicat softening temperature	--	ISO 306/B50	89.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	91.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220°C/10.0kg	ASTM D1238	39	g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ISO 1133	39	g/10min
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	112
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	114

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App