Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | ISO 60 | 0.60 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 11 g/10min |
| Melt volume flow rate | | ISO 11332 | 11.0 cm³/10min |
| saturation | | 4 | 0.0 % |
| balance | | 5 | 0.0 % |
| viscosity number | | ISO 307 | 91.0 cm³/g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ISO 2039-2 | 105 |
| ball-indentation hardness | | ISO 2039-1 | 150 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | ISO 121026 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-27 | 3300 MPa |
| yield | | ISO 527-2/5 | 43.0 MPa |
| yield | | ISO 527-28 | 42.0 MPa |
| yield | | ISO 527-29 | 2.0 % |
| fracture | | ISO 527-2/5 | 2.0 % |
| elongation | Break | ISO 527-210 | 2.0 % |
| Flexural modulus | | ISO 178 | 3500 MPa |
| bending strength | | ISO 178 | 80.0 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 6009317 | 1E+13 ohms |
| Volume resistivity | | IEC 6009318 | >1.0E+15 ohms·m |
| dielectric strength | | IEC 60243-119 | 140 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| flow | | 15 | 8E-05 cm/cm/°C |
| horizontal | | 16 | 8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare