PC EXL9112 GY SABIC INNOVATIVE US

Form：Granules | Grade：Injection grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	25	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	60	kJ/m²
Dart impact	23°C, Total Energy	ASTM D3763	67.0	J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	825	°C
Extreme Oxygen Index		ISO 4589-2	40	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--2	ASTM D638	2260	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2200	Mpa
tensile strength	Yield3	ASTM D638	58.0	Mpa
	tensile strength	Yield	ISO 527-2/50	59.0	Mpa
		tensile strength	Break3	ASTM D638	58.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	55.0	Mpa
elongation	Yield3	ASTM D638	5.8	%
	elongation	Yield	ISO 527-2/50	5.0	%
		elongation	Break3	ASTM D638	100	%
		elongation	elongation	Break	ISO 527-2/50	100	%
Bending modulus	50.0 mm Span4	ASTM D790	2330	Mpa
Bending modulus	Bending modulus	--5	ISO 178	2300	Mpa
bending strength	--5,6	ISO 178	88.0	Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	95.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			120	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Suggested injection volume			40 to 60	%
Temperature at the rear of the barrel			215 to 295	°C
Temperature in the middle of the barrel			280 to 305	°C
Temperature at the front of the material cylinder			295 to 315	°C
Spray nozzle temperature			290 to 310	°C
Processing (melt) temperature			295 to 315	°C
Mold temperature			70 to 95	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			40 to 70	rpm
Exhaust hole depth			0.025 to 0.076	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI		UL 746	130	°C
RTI Imp		UL 746	120	°C
RTI Elec		UL 746	130	°C
Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	7.5E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.2E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.5E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.2E-5	cm/cm/°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Vicat softening temperature	--	ISO 306/B120	144	°C
Vicat softening temperature	Vicat softening temperature	--	ASTM D152511	143	°C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span10	ISO 75-2/Ae	124	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	123	°C
		Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span10	ISO 75-2/Be	136	°C
		Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	136	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	17	g/10 min
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	16.0	cm3/10min
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.40 - 0.80	%
Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.80	%
Water absorption rate	Saturation, 23°C	ISO 62	0.35	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15	%
Outdoor applicability		UL 746C	f1
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1 MHz	IEC 60250	0.010
	Dissipation factor	60 Hz	IEC 60250	4.0E-4
	Dissipation factor	Dissipation factor	50 Hz	IEC 60250	4.0E-4
Relative permittivity	1 MHz	IEC 60250	2.70
	Relative permittivity	60 Hz	IEC 60250	2.70
	Relative permittivity	Relative permittivity	50 Hz	IEC 60250	2.70
Dielectric strength	3.20 mm, in Oil	IEC 60243-1	19	KV/mm
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H 358/30	ISO 2039-1	95.0	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC EXL9112 GY SABIC INNOVATIVE US

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index