PC Makrolon® 6557
48
- Properties:Medium viscosity
- Usages:Electrical fieldElectronic fieldIndustrial applications
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.20 g/cm³ | |
| Apparent density 2 | ISO60 | 0.64 g/cm³ | |
| melt mass-flow rate | ISO1133 | 10 g/10min | |
| Melt volume flow rate | ISO1133 | 10.0 cm3/10min | |
| Shrinkage rate | ISO2577 | 0.60to0.80 % | |
| ISO2577 | 0.60to0.80 % | ||
| ISO294-4 | 0.70 % | ||
| ISO294-4 | 0.65 % | ||
| Water absorption rate | ISO62 | 0.30 % | |
| ISO62 | 0.12 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO2039-1 | 115 Mpa |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Refractive Index11 | ISO489 | 1.586 | |
| transmissivity | ISO13468-2 | 89.0 % | |
| ISO13468-2 | 89.0 % | ||
| ISO13468-2 | 88.0 % | ||
| ISO13468-2 | 87.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL94 | V-2 | |
| UL94 | V-2 | ||
| UL94 | V-0 | ||
| Burning wire flammability index | IEC60695-2-12 | 900 °C | |
| IEC60695-2-12 | 960 °C | ||
| IEC60695-2-12 | 960 °C | ||
| needle flame test | IEC60695-11-5 | 2.0 min | |
| IEC60695-11-5 | 2.0 min | ||
| IEC60695-11-5 | 1.0 min | ||
| IEC60695-11-5 | 2.0 min | ||
| IEC60695-11-5 | 2.0 min | ||
| SelfIgnitionTemperature | ASTMD1929 | 530 °C | |
| Hot filament ignition temperature | IEC60695-2-13 | 875 °C | |
| IEC60695-2-13 | 875 °C | ||
| IEC60695-2-13 | 900 °C | ||
| Extreme Oxygen Index 10 | ISO4589-2 | 36 % | |
| ApplicationofFlamefromSmallBurner-Method | DIN53438-1,-3 | K1,F1 | |
| ISO3795 | passed | ||
| FlashIgnitionTemperature | ASTMD1929 | 460 °C | |
| GlowWireTest | EDFHN60E.02 | 750 °C | |
| EDFHN60E.02 | 750 °C | ||
| needle flame test | IEC60695-11-5 | 2.0 min |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ElectrolyticalCorrosion | IEC60426 | A1 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO527-2/1 | 2400 Mpa | |
| Tensile stress | ISO527-2/50 | 66.0 Mpa | |
| ISO527-2/50 | 70.0 Mpa | ||
| Tensile strain | ISO527-2/50 | 6.1 % | |
| ISO527-2/50 | 130 % | ||
| Nominal tensile fracture strain | ISO527-2/50 | >50 % | |
| TensileCreepModule | ISO899-1 | 2200 Mpa | |
| Tensile creep modulus | ISO899-1 | 1900 Mpa | |
| Flexural modulus | ISO178 | 2400 Mpa | |
| Bending stress | ISO178 | 75.0 Mpa | |
| ISO178 | 99.0 Mpa | ||
| ISO178 | 7.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam gap 6 | ISO7391 | 14 kJ/m² | |
| ISO7391 | 70 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO179/1eU | NoBreak | |
| ISO179/1eU | NoBreak | ||
| ISO179/1eU | NoBreak | ||
| Suspended wall beam gap impact strength 7 | ISO7391 | 12 kJ/m² | |
| ISO7391 | 65 kJ/m² | ||
| Multi axis Instrumented Impact Energy | ISO6603-2 | 65.0 J | |
| ISO6603-2 | 60.0 J | ||
| Multi axis Instrumented Peak Impact Force | ISO6603-2 | 6300 N | |
| ISO6603-2 | 5400 N |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| GasPermeation | ISO2556 | 650 cm³/m²/bar/24hr | |
| WaterVaporTransmission Rate | ISO15106-1 | 15 g/m²/24hr | |
| GasPermeation | ISO2556 | 16900 cm³/m²/bar/24hr | |
| ISO2556 | 3800 cm³/m²/bar/24hr | ||
| ISO2556 | 510 cm³/m²/bar/24hr | ||
| ISO2556 | 120 cm³/m²/bar/24hr | ||
| ISO2556 | 2760 cm³/m²/bar/24hr |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | IEC60250 | 8E-04 | |
| IEC60250 | 9E-03 | ||
| CTI | IEC60112 | 225 V | |
| IEC60112 | 125 V | ||
| Surface Resistivity | IEC60093 | 1E+16 ohms | |
| Volume resistivity | IEC60093 | 1E+16 ohms·cm | |
| dielectric strength | IEC60243-1 | 34 KV/mm | |
| IEC60250 | 3.10 | ||
| IEC60250 | 3.00 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO75-2/B | 136 °C | ||
| ISO75-2/A | 124 °C | ||
| Glass transition temperature 8 | ISO11357-2 | 144 °C | |
| vicat | ISO306/B50 | 143 °C | |
| ISO306/B120 | 144 °C | ||
| BallPressure Test | IEC60695-10-2 | Pass | |
| ISO11359-2 | 6.5E-05 cm/cm/°C | ||
| ISO11359-2 | 6.5E-05 cm/cm/°C | ||
| Thermal conductivity coefficient 9 | ISO8302 | 0.20 W/m/K | |
| RTI Elec | UL746 | 125 °C | |
| RTI Imp | UL746 | 115 °C | |
| RTI Str | UL746 | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.