PA66 FR50 BK505 DUPONT USA

234

Form：Granules | Grade：Injection grade

Properties:

Flame retardantGlass fiber reinforced

Typical Applications:

Fitness equipmentAutomotive sectorElectrical fieldElectronic fieldElectrical appliances

Supplier(8)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Fitness equipment \| Automotive sector \| Electrical field \| Electronic field \| Electrical appliances
Properties:	Flame retardant \| Glass fiber reinforced

Certificates

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			PA66.25％玻维增强.阻燃.注射成型
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-40°C	ISO 179/1eU	50	kJ/m²
	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	50	kJ/m²
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	60	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
FMVSS flammability		FMVSS302	B
Burning rate	1.00mm	ISO 3795	<100	mm/min
UL flame retardant rating	0.75mm	UL 94	V-0
	UL flame retardant rating	1.5mm	UL 94	V-0
		UL flame retardant rating	0.75mm	IEC 60695-11-10,-20	V-0
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	V-0
Extreme Oxygen Index		ISO 4589-2	35	%
UL flame retardant rating		UL 94	V-0
UL flame retardant rating	UL flame retardant rating		UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	10600	Mpa
tensile strength	Break	ISO 527-2	158	Mpa
Tensile strain	Break	ISO 527-2	2.1	%
Bending modulus		ISO 178	9410	Mpa
Impact strength of cantilever beam gap		ASTM D256/ISO 179	8.4	kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	7.9	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	2.1	%
Tensile modulus		ASTM D638/ISO 527	10640	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	158	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	9410	kg·cm/cm(J/M)ft·lb/in
Tensile modulus		ISO 527-2	10200	Mpa
tensile strength	Break	ISO 527-2	170	Mpa
Tensile strain	Break	ISO 527-2	2.6	%
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80	°C
Drying time - hot air dryer			2.0 to 4.0	hr
Suggested maximum moisture content			0.20	%
Processing (melt) temperature			280 to 300	°C
Melt Temperature, Optimum			290	°C
Mold temperature			70 to 120	°C
Mold Temperature, Optimum			100	°C
Maintain pressure			50.0 to 100	Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00	s/mm
Maximum Screw Tangential Speed			12	m/min
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	242	°C
Melting temperature		ISO 11357-3	260	°C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	2.1E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	2.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	MD：55to160°C	ISO 11359-2	1.2E-05	cm/cm/°C
			Linear coefficient of thermal expansion	TD：--	ISO 11359-2	7.9E-05	cm/cm/°C
				Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	6.9E-05	cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：55to160°C	ISO 11359-2	1.1E-04	cm/cm/°C
Combustibility (rate)		UL 94	V-0
Hot deformation temperature	HDT	ASTM D648/ISO 75	242	℃（℉）
Melting temperature			260	℃（℉）
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	240	°C
Melting temperature		ISO 11357-3	262	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Top out temperature			210	°C
Shrinkage rate	TD	ISO 294-4	0.70	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.30	%
density		ASTM D792/ISO 1183	1.60
Shrinkage rate		ASTM D955	0.3-0.7	%
	Shrinkage rate	横向Flow	ISO 294-4	0.80	%
	Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.30	%
Water absorption rate	24 hr, 23°C, 2.00 mm	ISO 62	0.60	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 62631-3-2	--	ohms
Volume resistivity		IEC 62631-3-1	> 1.0E+13	ohms·m
Dielectric strength	2.00 mm	IEC 60243-1	24	KV/mm
Compared to the anti leakage trace index		IEC 60112	PLC 2
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
EmissionofOrganicCompounds		VDA277	4.70	µgC/g
Odor		VDA270	4.50

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA66 FR50 BK505 DUPONT USA

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index