Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.14 -- |
| melt mass-flow rate | | g/10min | 15到25 -- |
| Shrinkage rate | | % | 1.0到1.3 -- |
| Water absorption rate | | % | 1.3 -- |
| HeatStability | | °C | 100 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 120 103 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | V-2 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | % | 50 250到300 |
| Flexural modulus | | MPa | 2900 1300 |
| bending strength | | MPa | 120 50.0 |
| Tensile modulus | | MPa | 3000 1500 |
| tensile strength | | MPa | 90.0 65.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| | kJ/m² | 6.0 12 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+15 -- |
| dielectric strength | | kV/mm | 21 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | 200 -- |
| | °C | 80.0 -- |
| melting temperature | | °C | 250到260 -- |
| | cm/cm/°C | 7E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare