Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 0.50 % |
| Shrinkage rate | | ISO 2577 | 0.50 % |
| Shrinkage rate | | ISO 2577 | 0.40 % |
| density | | ASTM D792 | 1.13 g/cm³ |
| density | | ISO 1183 | 1.13 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 19 g/10min |
| melt mass-flow rate | | ISO 1133 | 19 g/10min |
| Shrinkage rate | | ASTM D955 | 0.40 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 114 |
| Rockwell hardness | | ISO 2039-2 | 116 |
| Hardness | | JISK5401 | H |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2400 Mpa |
| Tensile modulus | | ISO 527-2/50 | 2600 Mpa |
| tensile strength | | ASTM D638 | 47.0 Mpa |
| tensile strength | | ISO 527-2/50 | 53.0 Mpa |
| tensile strength | | ASTM D638 | 29.0 Mpa |
| tensile strength | | ISO 527-2/50 | 38.0 Mpa |
| elongation | | ASTM D638 | 15 % |
| Tensile strain | | ISO 527-2/50 | 20 % |
| Flexural modulus | | ASTM D790 | 2500 Mpa |
| Flexural modulus | | ISO 178 | 2600 Mpa |
| bending strength | | ASTM D790 | 69.0 Mpa |
| bending strength | | ISO 178 | 80.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 120 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 88 J/m |
| Impact strength of cantilever beam gap | | ISO 180/1A | 10 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 93.0 °C |
| Heat distortion temperature | | ISO 75-2/B | 88.0 °C |
| Heat distortion temperature | | ASTM D648 | 84.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 76.0 °C |
| vicat | | ISO 306/B50 | 95.096.0 °C |
| vicat | | ISO 306/B120 | 98.099.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.