Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.24 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.30 % |
| Water absorption rate | Saturation | ASTM D570 | 0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 82 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ASTM D638 | 30 % |
| Flexural modulus | | ASTM D790 | 2690 MPa |
| bending strength | | ASTM D790 | 106 MPa |
| Tensile modulus | | ASTM D638 | 2480 MPa |
| tensile strength | Yield | ASTM D638 | 70.3 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 69 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | 1.0E+2到1.0E+3 ohms |
| Volume resistivity | | ASTM D257 | >1.0E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 17 kV/mm |
| dielectric constant | | ASTM D150 | 3.07 |
| dielectric constant | | ASTM D150 | 3.03 |
| Dissipation Factor | | ASTM D150 | 8E-04 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | 内部方法 | 160 °C |
| Heat distortion temperature | | ASTM D648 | 174 °C |
| Glass Transition Temperature | | ASTM D3418 | 190 °C |
| melting temperature | | ASTM D789 | 343to399 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 5.8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.