Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | DENKA Method | 0.5 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Total Light Transmittance | | ISO 13468-1(JIS K7361) | 91 % |
| Haze ratio | | ISO 14782(JIS 7136) | 1.3 % |
| other | Test Condition | Test Method | Test Result |
|---|
| | | 透明, 耐热 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133(JIS K7210) | 2.0 g/10min |
| melt mass-flow rate | | ISO 1133(JIS K7210) | 28 g/10min |
| density | | ISO 1183(JIS K7112) | 1106 kg/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile yield stress | | ISO 527-1,-2(JIS K7161,7162) | 48 Mpa |
| Flexural modulus | | ISO 178(JIS K7171) | 2300 Mpa |
| bending strength | | ISO 178(JIS K7171) | 74 Mpa |
| Gap Charpy impact strength | | ISO 179(JIS K7111) | 10 KJ/m |
| Rockwell hardness | | ISO 2039-2(JIS K7202) | 54 M |
| Rockwell hardness | | ASTM D785 | 54 |
| Flexural modulus | | ASTM D790/ISO 178 | 2300(MPa) kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 74(MPa) kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.1 |
| Mold Shrinkage | | ASTM D955 | 0.5 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Load deformation temperature | | ISO 75-1,-2(JIS K7191-1,-2) | 73 °C |
| vicat | | ISO 306(JIS K7206) | 93 °C |
| combustibility | | UL 94 | HB |
| Combustibility (rate) | | UL94 | HB |
| vicat | | ASTM D1525/ISO R306 | 93 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare