Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.75 g/cm³ |
| Shrinkage rate | | 内部方法 | 0.40to0.80 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ISO 2039-2 | 119 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO 527-2 | 1.0 % |
| Flexural modulus | | ISO 178 | 16500 MPa |
| bending strength | | ISO 178 | 230 MPa |
| tensile strength | | ISO 527-2 | 155 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 10 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| dielectric strength | | IEC 60243-1 | 22 kV/mm |
| dielectric constant | | ASTM D150 | 3.40 |
| Dissipation Factor | | ASTM D150 | 2E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ISO 75-2/B | 220 °C |
| Hot deformation temperature (HDT) | | ISO 75-2/A | 210 °C |
| melting temperature | | ISO 11357-3 | 220to250 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.