Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.16to1.18 g/cm³ |
| Shrinkage rate | | ASTM D955 | 1.0to1.5 % |
| Shrinkage rate | | ASTM D955 | 1.5to2.5 % |
| Water absorption rate | | ASTMD570 | 1.0to1.5 % |
| Water absorption rate | Saturation | ASTM D570 | 8.0 % |
| Water absorption rate | | ISO 62 | 8.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 775 °C |
| Limiting Oxygen Index | | ASTM D2863 | 32 % |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 3600 MPa |
| tensile strength | Yield | ASTMD638 | 95.0 MPa |
| tensile strength | Break | ASTMD638 | 85.0 MPa |
| elongation | Break | ASTMD638 | 6.0 % |
| Flexural modulus | | ASTMD790 | 3300 MPa |
| bending strength | | ISO 178 | 135 MPa |
| bending strength | Break | ASTM D790 | 135 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 50 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256 | 25 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 40 J/m |
| Charpy Notched Impact Strength | | ISO 179 | 2.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1E+15 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ASTMD648 | 225 °C |
| Hot deformation temperature (HDT) | | ASTMD648 | 90.0 °C |
| Continuous use temperature | | IEC 60216 | 80.0 °C |
| Continuous use temperature | | IEC 60216 | 120 °C |
| vicat | | ASTMD15256 | 248 °C |
| vicat | | ASTMD15257 | 236 °C |
| melting temperature | | ASTMD211 | 250to256 °C |
| | ASTM D696 | 8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.