PA46 46HF4130 DSM HOLAND

Form：Granules | Grade：Enhanced level

Properties:

High mobilityThermal stability

Typical Applications:

Home appliance componentsElectronic and electrical components

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Home appliance components \| Electronic and electrical components
Properties:	High mobility \| Thermal stability

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	60	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Flammability level		UL 94	HB
Flammability level	Flammability level		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ISO 178	9000	Mpa
Tensile strain	Break, 200°C	ISO 527-2	5.5	%
	Tensile strain	Break, 180°C	ISO 527-2	5.5	%
		Tensile strain	Break, 160°C	ISO 527-2	5.5	%
			Tensile strain	Break, 120°C	ISO 527-2	5.5	%
			Tensile strain	Tensile strain	Break	ISO 527-2	3.0	%
tensile strength	Break, 200°C	ISO 527-2	90.0	Mpa
	tensile strength	Break, 180°C	ISO 527-2	95.0	Mpa
		tensile strength	Break, 160°C	ISO 527-2	110	Mpa
			tensile strength	Break, 120°C	ISO 527-2	125	Mpa
			tensile strength	tensile strength	Break	ISO 527-2	210	Mpa
Tensile modulus	200°C	ISO 527-2	4500	Mpa
	Tensile modulus	180°C	ISO 527-2	4700	Mpa
		Tensile modulus	160°C	ISO 527-2	5000	Mpa
			Tensile modulus	120°C	ISO 527-2	5500	Mpa
			Tensile modulus	Tensile modulus	--	ISO 527-2	10000	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.5E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	6.0E-5	cm/cm/°C
RTI Elec		UL 746	65.0	°C
Thermal Index - 5000 hr		IEC 60216	177	°C
Melting temperature		ISO 11357-3	295	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	290	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	290	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.6	%
Shrinkage rate	Flow	ISO 294-4	0.50	%
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	1.3	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.