'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
POM 900P NC010 DUPONT NETHERLANDS
186
Form：Granules
Properties:
lubricationwear resistantHigh rigidityhigh strengthenhanceHigh impact resistanceHigh mobility
Typical Applications:
Home appliance componentsFiber gradeThin walled products
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Home appliance components | Fiber grade | Thin walled products |
| Properties: | lubrication | wear resistant | High rigidity | high strength | enhance | High impact resistance | High mobility |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 7.0 | kJ/m² |
| -40°C | ISO 180/1A | 8.0 | kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 200 | kJ/m² |
| -30°C | ISO 179/1eU | 200 | kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 | kJ/m² |
| -30°C | ISO 179/1eA | 7.0 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Burning rate | 1.00mm | ISO 3795 | 20 | mm/min |
| UL flame retardant rating | 0.8mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB | ||
| 0.8mm | IEC 60695-11-10,-20 | HB | ||
| 1.5mm | IEC 60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO 4589-2 | 23 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Atomization | F-value(refraction) | ISO 6452 | 95 | % |
| G-value(condensate) | ISO 6452 | 2E-04 | g | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Friction coefficient | vs.Itself-Dynamic,1hr | ASTM D1894 | 0.25 | |
| Bending modulus | ISO 178 | 3000 | Mpa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1500 | Mpa |
| 1hr | ISO 899-1 | 2800 | Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 23 | % | |
| Tensile modulus | ISO 527-2 | 3300 | Mpa | |
| tensile strength | Yield | ISO 527-2 | 71.0 | Mpa |
| Tensile strain | Yield | ISO 527-2 | 12 | % |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | MD：23to55°C | ASTME831 | 1E-04 | cm/cm/°C |
| Melting temperature | ISO 11357-3 | 178 | °C | |
| Vicat softening temperature | ISO 306/B50 | 160 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 94.0 | °C |
| 0.45MPa,Unannealed | ISO 75-2/B | 162 | °C | |
| Effective thermal diffusivity coefficient | 8E-08 | m²/s | ||
| AnnealingTime-Optional | 30.0 | min/mm | ||
| AnnealingTemperature | 160 | °C | ||
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1.2E-04 | cm/cm/°C |
| MD | ISO 11359-2 | 1.2E-04 | cm/cm/°C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | MD | ISO 294-4 | 1.9 | % |
| Water absorption rate | Saturation,23°C,2.00mm | ISO 62 | 1.4 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO 62 | 0.40 | % | |
| density | ISO 1183 | 1.42 | g/cm³ | |
| melt mass-flow rate | ISO 1133 | 25 | g/10min | |
| Melt Volume Flow Rate (MVR) | 190°C/2.16kg | ISO 1133 | 21.0 | cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.9 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Volume resistivity | IEC 60093 | 1E+14 | ohms·cm | |
| Surface resistivity | IEC 60093 | >1.0E+15 | ohms | |
| Relative permittivity | 100Hz | IEC 60250 | 3.80 | |
| 1MHz | IEC 60250 | 3.80 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Sale | ISO 2039-2 | 120 | |
| M-Sale | ISO 2039-2 | 92 | ||
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| EmissionofOrganicCompounds | VDA277 | 4.30 | µgC/g | |
| Emission | VDA275 | <8.00 | mg/kg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.