TPEE P40UX TOYOBO JAPAN
58
Form:Granules | Grade:Injection grade
Typical Applications:
Automotive interior partscurrency
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Automotive interior parts | currency |
Certificates
No Data...
Technical Data Sheet
| flammability | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | ||
| elastomer | Test Condition | Test Method | Test Result | Test Unit |
| Permanent compression deformation | JISK6301 | 50 | % | |
| tear strength | ASTM D624 | 98.0 | kN/m | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Bending modulus | ASTM D790 | 51.0 | Mpa | |
| elongation | Break | ASTM D638 | 690 | % |
| tensile strength | 50%Strain | ASTM D638 | 6.40 | Mpa |
| -- | ASTM D638 | 23.0 | Mpa | |
| Taber abraser | 1000Cycles | ASTM D1044 | 20.0 | mg |
| compressive strength | 10%Strain | ASTM D695 | 4.60 | Mpa |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | MD | ASTME831 | 1.7E-04 | cm/cm/°C |
| Melting temperature | DSC | 172 | °C | |
| Vicat softening temperature | ASTM D1525 | 120 | °C | |
| Brittle temperature | JISK6301 | <-65.0 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ASTM D648 | <25.0 | °C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | Equilibrium,23°C,65%RH | ASTM D570 | 0.48 | % |
| Shrinkage rate | MD:2.00mm | ASTM D955 | 0.50 | % |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 10 | g/10min |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dielectric strength | JISK2111 | 20 | KV/mm | |
| Volume resistivity | ASTM D257 | 2E+12 | ohms·cm | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Shore hardness | ShoreD | ASTM D2240 | 38 | |
| ShoreA | JISK6301 | 89 | ||
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| Resilience | JISK6301 | 78 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.