PET 130 BK112 BASF USA

Form：Granules | Grade：Enhanced level

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75 mm	UL 94	HB
	UL flame retardant rating	1.5 mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ISO 527-2	10200	Mpa
tensile strength	Break, 23°C	ASTM D638	145	Mpa
	tensile strength	Break, -40°C	ISO 527-2	211	Mpa
		tensile strength	Break, 120°C	ISO 527-2	54.0	Mpa
		tensile strength	tensile strength	Break, 150°C	ISO 527-2	42.0	Mpa
elongation	Break, 23°C	ASTM D638	3.0	%
	elongation	Break, -40°C	ISO 527-2	2.3	%
		elongation	Break, 120°C	ISO 527-2	4.0	%
		elongation	elongation	Break, 150°C	ISO 527-2	4.0	%
Bending modulus	23°C	ASTM D790	8760	Mpa
Bending modulus	Bending modulus	23°C	ISO 178	8250	Mpa
bending strength	23°C	ASTM D790	230	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			120	°C
drying time			2.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Processing (melt) temperature			280 to 300	°C
Mold temperature			100 to 110	°C
Injection pressure			3.50 to 12.5	Mpa
Injection speed			快速
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed	ASTM D648	235	°C
	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	240	°C
		Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	215	°C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	210	°C
Melting temperature		ASTM D3418	245	°C
Linear coefficient of thermal expansion	Flow	ASTM E831	2.3E-5	cm/cm/°C
RTI Elec	0.75 mm	UL 746	140	°C
	RTI Elec	1.5 mm	UL 746	140	°C
	RTI Elec	RTI Elec	3.0 mm	UL 746	140	°C
RTI Imp	0.75 mm	UL 746	140	°C
	RTI Imp	1.5 mm	UL 746	140	°C
	RTI Imp	RTI Imp	3.0 mm	UL 746	140	°C
RTI	0.75 mm	UL 746	140	°C
	RTI	1.5 mm	UL 746	140	°C
	RTI	RTI	3.0 mm	UL 746	140	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	3.18 mm，Flow		0.40	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity	1.50 mm	ASTM D257	> 1.0E+13	ohms·cm
Volume resistivity	Volume resistivity	--	IEC 60093	> 1.0E+13	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.