Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792,ISO1183 | 1.06 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 50到70 g/10min |
| melt mass-flow rate | | ISO1133 | 40 g/10min |
| Shrinkage rate | | ASTMD955 | 0.40到0.70 % |
| Shrinkage rate | | ISO294-4 | 0.40到0.70 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTMD790 | 1900 MPa |
| Flexural modulus | | ISO178 | 1750 MPa |
| bending strength | | ASTMD790 | 60.0 MPa |
| bending strength | | ISO178 | 65.0 MPa |
| tensile strength | | ASTMD638,ISO527-2/50 | 45.0 MPa |
| elongation | Break | ASTMD638 | >50 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 5.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179 | 20 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256 | 250 J/m |
| Impact strength of cantilever beam gap | | ISO180 | 18 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | >1.0E+14 ohms |
| Volume resistivity | | IEC60093 | >1.0E+14 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 90.0 °C |
| | ISO75-2/A | 60.0 °C |
| vicat | | ISO306/B50,ASTMD15256 | 95.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare