ABS 0824V
0
- Properties:Low gloss and good fluidity
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 6.5-9.5 g/10min | |
| Shrinkage rate | 0.4-0.6 % | ||
| Water absorption rate | Equilibrium | ASTM D-570 | 0.3 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTM D-523 | 40 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield | ASTM D-638 | 27 MPa |
| elongation | Break | ASTM D-638 | 100 % |
| Flexural modulus | ASTM D-790 | 1550 MPa | |
| bending strength | Yield | ASTM D-790 | 40 MPa |
| Charpy Notched Impact Strength | DIN 53453 | 9 Kj/m² | |
| Impact strength of cantilever beam gap | ISO 180 | 7 Kj/m² | |
| Rockwell hardness | ISO 2039-2 | 97 |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | Flow | ASTM D696 | 9E-05 cm/cm/℃ |
| thermal conductivity | ASTM C177 | 0.17 W/m/K | |
| vicat | ASTM D-1525 | 97 ℃ | |
| Hot filament ignition temperature | IEC 60695-2-1 | 650 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.