PAI TORLON® 4301
105
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.35-0.60 % | |
| Water absorption rate | ASTM D570 | 0.28 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 6830 Mpa | |
| ASTM D1708 | 6550 Mpa | ||
| tensile strength | ASTM D638 | 113 Mpa | |
| ASTM D1708 | 163 Mpa | ||
| elongation | ASTM D638 | 3.3 % | |
| ASTM D1708 | 7.0 % | ||
| Flexural modulus | ASTM D790 | 6890 Mpa | |
| ASTM D790 | 4960 Mpa | ||
| bending strength | ASTM D790 | 215 Mpa | |
| ASTM D790 | 112 Mpa | ||
| Compression Modulus | ASTM D695 | 5310 Mpa | |
| compressive strength | ASTM D695 | 166 Mpa | |
| coefficient of friction | ASTM D3702 | 0.31 | |
| ASTM D3702 | 0.39 | ||
| ASTM D3702 | 0.18 | ||
| ASTM D3702 | 0.030 | ||
| Wear factor | ASTM D3702 | 17.0 in³·min^-10/ft·lb·hr | |
| ASTM D3702 | 14.0 in³·min^-10/ft·lb·hr | ||
| ASTM D3702 | 9.00 in³·min^-10/ft·lb·hr | ||
| ASTM D3702 | 0.400 in³·min^-10/ft·lb·hr |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D256 | 410 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 8E+17 ohms | |
| Volume resistivity | ASTM D257 | 8E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 279 °C | |
| thermal conductivity | ASTMC177 | 0.53 W/m/K | |
| Linear coefficient of thermal expansion | ASTM D696 | 2.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.