PA6 BKV15H1.0 LANXESS GERMANY

Form：Granules | Grade：Injection grade

Properties:

Glass fiber reinforced

Typical Applications:

Home appliance componentsAutomotive ApplicationsElectronic and electrical components

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Home appliance components \| Automotive Applications \| Electronic and electrical components
Properties:	Glass fiber reinforced

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			注射级.15%玻纤
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength		ASTM D256/ISO 179	45	kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	30	kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap		ASTM D256/ISO 179	40	kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	35	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	3	%
Tensile modulus		ASTM D638/ISO 527	6300	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	125	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	5600	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	200	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	HDT	ASTM D648/ISO 75	-190	℃（℉）
Melting temperature			213	℃（℉）
Vicat softening temperature		ASTM D1525/ISO R306	>200	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	0.3	mm/mm.℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		ASTM D955	0.19	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.