PA46 TS341 DSM HOLAND

Form：Granules

Properties:

Glass fiber reinforcedThermal stability

Typical Applications:

Home appliance componentsElectronic and electrical components

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Home appliance components \| Electronic and electrical components
Properties:	Glass fiber reinforced \| Thermal stability

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
flammability	Test Condition	Test Method	Test Result	Test Unit
Flammability level		UL 94	V-2
Flammability level	Flammability level		UL 94	V-2
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--	ISO 527-2	3300	Mpa
	Tensile modulus	120°C	ISO 527-2	800	Mpa
		Tensile modulus	160°C	ISO 527-2	650	Mpa
			Tensile modulus	180°C	ISO 527-2	600	Mpa
			Tensile modulus	Tensile modulus	200°C	ISO 527-2	500	Mpa
tensile strength	Yield	ISO 527-2	100	Mpa
	tensile strength	Yield, 120°C	ISO 527-2	50.0	Mpa
		tensile strength	Yield, 160°C	ISO 527-2	40.0	Mpa
			tensile strength	Yield, 180°C	ISO 527-2	35.0	Mpa
			tensile strength	tensile strength	Yield, 200°C	ISO 527-2	30.0	Mpa
Nominal tensile fracture strain	--	ISO 527-2	40	%
	Nominal tensile fracture strain	120°C	ISO 527-2	> 50	%
		Nominal tensile fracture strain	160°C	ISO 527-2	> 50	%
			Nominal tensile fracture strain	180°C	ISO 527-2	> 50	%
			Nominal tensile fracture strain	Nominal tensile fracture strain	200°C	ISO 527-2	> 50	%
Bending modulus	--	ISO 178	3000	Mpa
	Bending modulus	120°C	ISO 178	800	Mpa
	Bending modulus	Bending modulus	160°C	ISO 178	600	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	280	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	190	°C
Melting temperature		ISO 11357-3	295	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	8.5E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.1E-4	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	横向Flow	ISO 294-4	2.0	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	2.0	%
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	3.7	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	25	KV/mm
Relative permittivity	100 Hz	IEC 60250	4.00
Relative permittivity	Relative permittivity	1 MHz	IEC 60250	3.60

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.