ABS GA-501 NIPPON A&L

Form：Granules | Grade：Injection grade

Properties:

High impactHigh toughness

Typical Applications:

chipProfilefilmBag

Supplier(0)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	chip \| Profile \| film \| Bag
Properties:	High impact \| High toughness

Certificates

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			撞击性高
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220℃/10kg	ASTM D-1238	32	g/10min
density	23℃	ASTM D-792	1.04	23℃
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ASTM D785	113
Bending modulus		ASTM D790/ISO 178	2350	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	67	kg/cm²(MPa)[Lb/in²]
tensile strength	23℃	ASTM D-638	47	Mpa
Elongation at Break	23℃	ASTM D-638	20	%
Bending modulus	23℃	ASTM D-790	2250	Mpa
bending strength	23℃	ASTM D-790	62	Mpa
Impact strength of cantilever beam gap	23℃ 6.4mmt	ASTM D-256	294	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30℃,6.4mmt	ASTM D-256	127	J/m
Rockwell hardness	23℃	ASTM D-785	113	R-Scale
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL 94	HB
Hot deformation temperature	1.82Mpa	ASTM D-648	85	°C
Vicat softening temperature	1.0kgf	ASTM D-1525	105	°C
Ball indentation temperature			90	°C
UL flame retardant rating		UL 94	HB	calss
Forming temperature			200-260	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.04
Shrinkage rate		ASTM D-955	0.4-0.6	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.