thermosetting | Test Condition | Test Method | Test Result |
---|
Thermosetting components | | | 10to35 min |
Thermosetting components | | | 400to600 cP |
Thermosetting components | Resin | | 100 |
Thermosetting components | Hardener | | 按重量计算的混合比:43 |
physical property | Test Condition | Test Method | Test Result |
---|
Water absorption rate | | | 0.30 % |
Cured Properties | Test Condition | Test Method | Test Result |
---|
elongation | Break | ISO 527 | 2.0 % |
dielectric strength | | IEC 60243 | 34 kV/mm |
relative permittivity | | IEC 60250 | 3.70 |
Volume resistivity | | IEC 60093 | 7E+14 ohms·cm |
Shore hardness | | ISO 868 | 85to90 |
tensile strength | | ISO 527 | 54.0 MPa |
Uncured Properties | Test Condition | Test Method | Test Result |
---|
density | | | 1.20to1.24 g/cm³ |
density | | | 1.53to1.57 g/cm³ |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | V-0 |
Supplementary Information | Test Condition | Test Method | Test Result |
---|
operate temperature | | | -40-145 °C |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Glass Transition Temperature | | TMA | 85.0 °C |
thermal conductivity | | ISO 22007-2 | 0.55 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.