Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 11 g/10min |
| Shrinkage rate | | ASTM D955 | 0.50to0.80 % |
| density | | ASTM D792 | 1.20 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 118 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 61.8 MPa |
| elongation | | ASTM D638 | >150 % |
| Flexural modulus | | ASTM D790 | 2260 MPa |
| bending strength | | ASTM D790 | 98.1 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 740 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 2E+17 ohms·cm |
| dielectric strength | | ASTM D149 | 17 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI Imp | | UL 746 | 130 °C |
| RTI Str | | UL 746 | 130 °C |
| Heat distortion temperature | | ASTM D648 | 130 °C |
| vicat | | ASTM D15255 | 141 °C |
| RTI Elec | | UL 746 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.