POM HOSTAFORM® C9021 SW
33
- Properties:wear resistantcurrency
- Usages:Household appliancesHousehold appliancesAutomotive sectorFitness equipmentThin walled products
Compare
View PricesTechnical Data Sheet
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.42 g/cm | |
| melt mass-flow rate | ISO 1133 | 9.94 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy without notch impact strength | ISO 179 1eU | 9.0 J/cm | |
| Charpy notch impact strength | ISO 179 1eA | 0.4 J/cm | |
| Charpy without notch impact strength | ISO 179 1eU | 8.50 J/cm | |
| Charpy notch impact strength | ISO 179 1eA | 0.4 J/cm | |
| Tensile creep modulus | ISO 899 part 1 | 2400 Mpa | |
| ISO 899 part 1 | 1200 Mpa | ||
| ball indentation hardness | ISO 2039 part 1 | 135 Mpa | |
| Yield tensile strength | ISO 527 part 1/2 | 53 Mpa | |
| elongation at break | ISO 527 part 1/2 | 16 % | |
| elongation | ISO 527 part 1/2 | 7.0 % | |
| Tensile modulus | ISO 527 part 1/2 | 2850 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 11359 part 1/2 | 120 µm/m-℃ | ||
| melting point | ISO 3146 method C1b | 166 °C | |
| ISO 75 part 1/2 | 80 °C | ||
| vicat | ISO 306 | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.