PEEK 770CA30 JILIN JOINATURE

Form：Granules | Grade：Injection grade

Properties:

Carbon fiber reinforcedenhance

Typical Applications:

AerospaceWire and cableAutomotive sectorNursing suppliesMedical suppliesElectronic fieldElectrical field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Aerospace \| Wire and cable \| Automotive sector \| Nursing supplies \| Medical supplies \| Electronic field \| Electrical field
Properties:	Carbon fiber reinforced \| enhance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength		ISO 179-1eA	7	kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1U	45	kJ/m²
Suspended wall beam without notch impact strength		ISO 180/U	45	kJ/m²
Impact strength of cantilever beam gap		ISO 180/A	9	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Break，23℃	ISO 527	260	Mpa
bending strength	Break，23℃	ISO 178	380	Mpa
Bending modulus	23℃	ISO 178	23000	Mpa
Tensile strain	Break，23℃	ISO 527	1.7	%
compressive strength	23℃	ISO 604	300	Mpa
Shore hardness	23℃	ISO 868	88	D 级
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 Mpa	ISO 75-f	336	°C
Linear coefficient of thermal expansion	高于Tg沿着Flow	ISO 11359	6	ppm/K
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	低于Tg沿着Flow	ISO 11359	5	ppm/K
specific heat	23℃	DSC	1.8	kJ/kg /℃
Tg (initial)		ISO 11357	143	°C
Melting temperature		ISO 11357	343	°C
thermal conductivity	23℃	ISO 22007-4	0.95	W/m/K
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density	结晶	ISO 1183	1.4	g/cm³
melt mass-flow rate	380℃，5.0kg	ISO 1133	2.3	g/10min
Shrinkage rate	TD	ISO 294-4	0.1	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.5	%
Water absorption rate	Equilibrium，23℃	ISO 62-1	0.3	%
Water absorption rate	Water absorption rate	23℃，24hr，3.2 mm厚拉伸棒	ISO 62-1	0.04	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity	23 ℃，1V	IEC 60093	10^5	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.