Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D570 | 0.010 % |
| Water absorption rate | Saturation | ASTM D570 | 0.010 % |
| density | | ASTM D792 | 1.68 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 75 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 1650 MPa |
| tensile strength | Ultimate | ASTM D638 | 31.0 MPa |
| elongation | Break | ASTM D638 | 200 % |
| Flexural modulus | | ASTM D790 | 1650 MPa |
| bending strength | Yield | ASTM D790 | 48.3 MPa |
| compressive strength | | ASTM D695 | 34.5 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | 内部方法 | >1.0E+13 ohms |
| dielectric strength | | ASTM D149 | 20 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | ASTMF433 | 0.22 W/m/K |
| Heat distortion temperature | | ASTM D648 | 76.7 °C |
| Maximum operating temperature LongTerm, Air | | | 149 °C |
| Crystallization peak temperature | | ASTM D3418 | 240 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 1.2E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.