PFA NEOFLON® AP-201 DAIKIN JAPAN
103
- Properties:High temperature strengthcopolymerHigh mobilityGood liquidityHigh transparency
- Usages:Wire sheath
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792 | 2.14 到 2.16 | g/cm³ | |
| Apparent density | JIS K6891 | 1.00 到 1.40 | g/cm³ | |
| Melt mass flow rate | 372℃，5.0kg 372℃/5.0 kg | ASTM D1238 | 20 到 30 | g/10min |
| Water absorption rate | 饱和 饱和 | ASTM D570 | < 0.010 | % |
| Apparent viscosity of melt | 380℃ 380℃ | 2.00E+6 到 2.50E+7 | mPa·s |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 无断裂 | ||
| Shore hardness | 邵氏 D 邵氏 D | ASTM D2240 | 60 到 70 | |
| tensile strength | 屈服 屈服 | JIS K6891 | 24.5 到 29.4 | Mpa |
| Tensile strain | 断裂 断裂 | JIS K6891 | 350 到 450 | % |
| Bending modulus | ASTM D790 | 580 到 690 | Mpa | |
| Compressive modulus | ASTM D695 | 490 到 590 | Mpa | |
| compressive strength | 1% 应变 1% Strain | ASTM D695 | 4.90 到 5.90 | Mpa |
| 25% 应变 25% Strain | ASTM D695 | 31.4 到 33.3 | Mpa | |
| friction coefficient | 与钢 - 静态 与钢 - 静态 | 0.040 到 0.050 | ||
| Load deformation | 25℃，14 MPa 25°C, 14 MPa 2 2 | ASTM D621 | 2.50 到 3.00 | % |
| 25℃，14 MPa 25°C, 14 MPa 3 3 | ASTM D621 | 8.00 到 9.00 | % | |
| 100℃，6.9 MPa 100°C, 6.9 MPa 2 2 | ASTM D621 | 2.00 到 3.00 | % | |
| 100℃，6.9 MPa 100°C, 6.9 MPa 3 3 | ASTM D621 | 8.50 到 9.50 | % | |
| bending strength | ASTM D790 | No break |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature | ASTM D4591 | 300 到 310 | °C | |
| Linear coefficient of thermal expansion | MD：20~100℃ MD：20 到 100℃ | ASTM D696 | 0.00012 | 1/℃ |
| Specific Heat | 1050 | J/kg/℃ | ||
| Thermal Conductivity | ASTM C177 | 0.26 | W/m/K |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 1.60 mm 1.6 mm | UL 94 | V-0 | ||
| Extreme Oxygen Index | 1.57 mm 1.57 mm | ASTM D2863 | > 95 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.