Technical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|
| 收缩率 | TD | ISO294-4 | 0.70到1.3 % |
| 收缩率 | MD | ISO294-4 | 0.10到0.40 % |
| 热性能 | Test Condition | Test Method | Test Result |
|---|
| 熔融温度 | | ISO11357-3 | 225 °C |
| 热变形温度 | 1.8MPa,未退火 | ISO75-2/A | 150 °C |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|
| UL阻燃等级 | | UL94 | HB |
| 充模分析 | Test Condition | Test Method | Test Result |
|---|
| MeltViscosity | 260°C | ISO11443 | 185 Pa·s |
| 电气性能 | Test Condition | Test Method | Test Result |
|---|
| 表面电阻率 | | IEC60093 | 1E+13 ohms |
| 体积电阻率 | | IEC60093 | 1E+14 ohms·cm |
| 介电强度 | 2.00mm | IEC60243-1 | 23 KV/mm |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| 拉伸模量 | 23°C | ISO527-2 | 5800 Mpa |
| 拉伸应力 | 断裂,23°C | ISO527-2 | 80.0 Mpa |
| 拉伸应变 | 断裂,23°C | ISO527-2 | 2.8 % |
| 弯曲模量 | 23°C | ISO178 | 4200 Mpa |
| 弯曲应力 | 23°C | ISO178 | 110 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.