SPS C132 IDEMITSU JAPAN

192

Form：Granules

Properties:

enhanceGlass fiber reinforcedHigh temperature resistan

Typical Applications:

Household goods

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Household goods
Properties:	enhance \| Glass fiber reinforced \| High temperature resistan

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180	36	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	43	kJ/m²
machinability	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD		0.35	%
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75mm	UL 94	HB
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate			0.05	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Break		2.3	%
Tensile strength			105	Mpa
Bending modulus			8100	Mpa
bending strength			165	Mpa
Impact strength of cantilever beam gap	3.2mm 没有Notch		40	KJ/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	4mm 有Notch		10	KJ/m
bending strength		ISO 178	185	Mpa
Bending modulus		ISO 178	9200	Mpa
Tensile strain	Break	ISO 527-2	2.1	%
tensile strength	Break	ISO 527-2	120	Mpa
Tensile modulus		ISO 527-2	9700	Mpa
Elongation at Break		ASTM D638/ISO 527	2.1	%
tensile strength		ASTM D638/ISO 527	120	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	70
Bending modulus		ASTM D790/ISO 178	9.2	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	185	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Elec		UL 746	50.0	°C
Linear coefficient of thermal expansion	TD：-30to30°C	TMA	3.9E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-30to30°C	TMA	1.8E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	240	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	265	°C
	Hot deformation temperature	Hot deformation temperature	HDT		235	°C
Combustibility	1/32英寸	UL 94	HB
RTI Imp		UL 746	50.0	°C
RTI Str		UL 746	50.0	°C
Combustibility (rate)		UL 94	HB/0.80
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	MD 1.8	mm/mm.℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD	Internal Method	0.50-0.80	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.010	%
Shrinkage rate	MD	Internal Method	0.10-0.40	%
density		ASTM D792/ISO 1183	1.25
Shrinkage rate		ASTM D955	MD 0.1-0.4	%
Water absorption rate		ASTM D570/ISO 62	0.01	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	>1.0E+16	ohms·cm
Dielectric strength		ASTM D149	45	KV/mm
Dielectric constant	1MHz	IEC 60250	2.90
Dissipation factor	1MHz	IEC 60250	<1.0E-3
Arc resistance		ASTM D495	PLC6
Compared to the anti leakage trace index	CTI)3	IEC 60112	PLC 1
Arc resistance		ASTM D495/IEC 60112	120
Volume resistivity		ASTM D257/IEC 60093	>1.0*10^16	Ω.cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.