Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.49 g/cm³ |
| Shrinkage rate | | | 0.50to0.70 % |
| density | | ASTM D792 | 1.49 g/cm³ |
| Shrinkage rate | | | 0.50to0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 107 |
| Rockwell hardness | | ASTM D785 | 107 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| exothermic | | FAR25.853 | <65 kW·min/m² |
| exothermic | | FAR25.853 | <65 kW/m² |
| exothermic | | FAR25.853 | <65 kW·min/m² |
| exothermic | | FAR25.853 | <65 kW/m² |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| smoke density | | ASTMF814 | <100 |
| smoke density | | ASTMF814 | <200 |
| smoke density | | ASTMF814 | 168to188 °C |
| smoke density | | ASTMF814 | <200 |
| smoke density | | ASTMF814 | 168to188 °C |
| smoke density | | ASTMF814 | <100 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | Yield | ASTM D790 | 60.0 MPa |
| tensile strength | Yield | ASTM D638 | 37.9 MPa |
| Flexural modulus | | ASTM D790 | 2830 MPa |
| bending strength | Yield | ASTM D790 | 60.0 MPa |
| tensile strength | Yield | ASTM D638 | 37.9 MPa |
| Flexural modulus | | ASTM D790 | 2830 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 270 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 270 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 76.7 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 3E-05 cm/cm/°C |
| Heat distortion temperature | | ASTM D648 | 76.7 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.